Gray Iron Castings With High Plasticity And High Toughness

In the production of Gray Iron Castings, the common casting defects are: stomata, composition and performance failure, hot cracking and cold cracking, shrinkage and shrinkage, slag and iron beans, cold and pouring inadequate, trachoma and sand, Multi-meat and the wrong radiation, deformation and so on. In general, the causes of these defects are not only the problem of molding core, but also the problems of many production processes such as smelting casting, sand quality, sand removal and so on, and therefore must be analyzed in order to take appropriate reasonable measures to solve them.

First, sand core and sand type of rigidity

After the sand casting, due to the static pressure of the molten iron or solidification caused by the expansion force, often resulting in wall movement and sand core collapse, which will make the casting of internal shrinkage and surface shrinkage. Therefore, in order to stabilize the casting size, it is necessary to maximize the mold.

In order to save the shape of materials, core manufacturing widely used hollow core, it is lighter than the solid core, so the heat capacity is small, solidification speed is slow, which will lead to sand expansion or sand core collapse. In addition, the molten iron may penetrate the hollow portion through the crack on the core or the core, which also causes the casting to be defective.

In order to improve the rigidity of hollow core, can be wet sand or sodium silicate sand filling; can also be made in half of the shell core, the internal set of ribs, after the core can be bonded hard core.

Second, the correct choice of pouring temperature

1. Phenomenon may occur when the pouring temperature is too low

(1) Manganese sulfide stomata This stomata is located below the casting surface and more in the above, often exposed after processing, stomatal diameter of about 2 ~ 6mm. Sometimes the pores contain a small amount of slag, metallographic studies show that this defect is MnS segregation and slag mixing, because the pouring temperature is low, while the molten iron containing Mn and S high.

(2) liquid slag processing after casting under the skin will find a single hole, the hole diameter is generally 1 ~ 3mm. In some cases there are only 1 to 2 holes. Metallographic studies have shown that these pores appear with a small amount of liquid slag, but no segregation of S is found.

(3) sand core gas caused by the pores and porous air holes often due to poor sand core caused by exhaust. Because the core when the sand core in the core box in the hardening, which often makes the sand core exhaust number is not enough. In order to form the exhaust hole, the core can be added after drilling hardening.

The most common cause of pouring temperature is that before pouring, the molten iron is transported and stopped for a long time in the open ladle. With a ladle cover with a thermal insulation material,Gray Iron Castings the heat loss can be significantly reduced.

Gray iron castings in the production of industrial machinery manufacturing widely used, there are many kinds of production processes, today, Xiaobian to take you to understand the Gray Iron Castings heat treatment process applications.

1, high temperature graphite annealing for the matrix structure contains more eutectic cementite castings to reduce the hardness and improve the machinability.

2, low temperature graphite annealing for gray iron casting hardness is too high, the matrix structure is not eutectic cementite, requires a high plasticity and high toughness of the gray iron castings.

3, to stress annealing for casting, casting welding, machining and other residual stress, to ensure that the gray iron castings and dimensional stability.

4, fully austenitized normalizing for the excessive amount of ferrite,Gray Iron Castings the hardness of the Gray Iron Castings, to improve the strength of gray iron cast, hardness and wear resistance.

5, part of the austenitic normalizing for the matrix is relatively uniform, and requires a certain strength and toughness of the gray iron castings.

6, complete austenitic quenching, tempering for the use of different tempering temperature of the matrix structure, to improve the strength of gray iron cast, hardness and wear resistance.

7, fully austenitic isothermal quenching for obtaining bainite matrix, improve the overall performance of gray iron castings.

8, surface hardening used to improve the strength of gray iron casting, surface strength and wear resistance.

9, chemical heat treatment for the gray iron castings surface special physical, chemical and mechanical properties.


Contact Us

Address:No,1188 , Meihe Rd, Jinhua City, Zhejiang Province , 321017,China

Tel:+86-0579-83930777

Fax:+86-0579-83930555

E-mail:sales@zjfourslar.com

Feedback!

Company Info

ZHEJIANG BO XING INDUSTRY AND TRADE CO., LTD, proformly called “ZHEJIANG SIXING MACHINING CO., LTD”was founded in 1995, is located in Jinhua city, Zhejiang Province.,There are 400 kilometers from Shanghai port , and about 250 kilometers from Ningbo port in distance.
. Our company covers an area about 35000 square meters with total assets about RMB 150 million Yuan, the building area is about 27000 square meters. There are 550 employees, including more than 60 people who are senior and middle level professional persons.
The Company specialized in producing camshafts and balance shafts of car engines, motorcycle engines, general-use gasoline engines, diesel engine. the annual productivity is about 4.5 million pieces. it has a regular organization, which consists of nine functional departments,, a foundry, three machine plants in the company .
Our company has 450 sets of various types of production equipment, such as CNC cam grinding machines,, CNC lathes, CNC hobbing machines, CNC gear shaving machines, CNC cylindrical grinders, CNC milling machines,, automatic washing machine, etc. The equipment number centralized ratio is over 75%, in 2012s, we company purchese one set of auto cam grinder from Toyoda of Japan whose number is GC20M-63 .
It has enough capability for self-supporting the blank of camshafts and cast pieces. The company's foundry is equipped with a vertical-type non-pressure molding line box shot (ZZ416A) and has an annual output